| Product Name | Chemistry Component (wt%) | Size | Melting Point | Apparent Density | Flow Rate | Properties | Pack | |
|---|---|---|---|---|---|---|---|---|
| Electrolytic Copper |
Cu ≥ 99.6 Fe ≤ 0.02 Pb ≤ 0.05 As ≤ 0.005 Sb ≤ 0.01 O ≤ 0.1 S ≤ 0.004 Water ≤ 0.05 |
-80 -200 -325 |
2.0-2.5 1.5-1.9 1.3-1.7 |
Ligh Rose Red Arborization Powder | 2KG/Vacuum bag (with iron bucket or carton), 40KG/Bucket | |||
| Atomized Copper |
Cu ≥ 99.5 Fe ≤ 0.02 Pb ≤ 0.05 As ≤ 0.005 Sb ≤ 0.01 O ≤ 0.20 S ≤ 0.004 Water ≤ 0.05 |
-80 -200 -325 |
2.5-3.5 2.3-3.0 2.3-2.9 |
Ligh Rose Red Irregular Spherality Shape | 2KG/Vacuum bag (with iron bucket or carton), 40KG/Bucket | |||
| Copper Base Alloy CuSn10 | Cu: 89-91 Sn: 9-11 |
-200 -325 |
3.0 – 4.0 3.2 – 4.3 |
Most are spherality shape with high flow rate and high apparent density | 2KG/Vacuum bag (with iron bucket or carton), 40KG/Bucket | |||
| Copper Base Alloy CuSn15 | Cu: 84-86 Sn: 14-16 |
-200 -325 |
3.3 – 4.0 3.3 – 4.0 |
Most are spherality shape with high flow rate and high apparent density | 2KG/Vacuum bag (with iron bucket or carton), 40KG/Bucket | |||
| Copper Base Alloy CuSn20 | Cu: 79-81 Sn: 19-21 |
-200 -325 |
3.5 – 4.5 3.5 – 4.5 |
Most are spherality shape with high flow rate and high apparent density | 2KG/Vacuum bag (with iron bucket or carton), 40KG/Bucket | |||
| Copper Base Alloy 663 | Cu: 85 Sn: 6 Zn: 6 Pb: 3 |
-80 -100 -200 -325 |
>4.5 3.0-4.0 3.0-4.0 3.2-4.0 |
Most are spherality shape with high flow rate and high apparent density | 2KG/Vacuum bag (with iron bucket or carton), 40KG/Bucket | |||
| Copper Base Alloy Cu80Zn20 | Cu: 79-81 Zn: 19-21 | -200 | 2.0 – 2.4 | Most are spherality shape with high flow rate and high apparent density | 2KG/Vacuum bag (with iron bucket or carton), 40KG/Bucket | |||