| Brand |
Product Name |
Chemistry (wt%) |
Hardness |
Temperature |
Properties & Application |
| C |
Cr |
Si |
Fe |
B |
Ni |
| KF-Ni15 |
NiCrBSiFe |
0.15 |
5 |
2 |
5 |
1 |
Bal. |
HRC 15 |
≤ 700ºC |
•Oxy-Acetylene, PTA, HVOF, APS, laser cladding, self-fluxing, spherical
•Glass molds, bearings
•Low hardness, high toughness
•Good corrosion resistance and wetability
|
| KF-Ni25 |
NiCrBSiFe |
0.20 |
7 |
2.8 |
5 |
1.5 |
Bal. |
HRC25 |
≤ 700ºC |
•Oxy-Acetylene, PTA, HVOF, APS, laser cladding, self-fluxing, spherical
•Glass molds, bearings
•Low hardness, high toughness
•Good oxidation and corrosion resistance as well as wetability
•Exellent machinability
|
| KF-Ni35 |
NiCrBSiFe |
0.30 |
9 |
3 |
5 |
2 |
Bal. |
HRC 35 |
≤ 650ºC |
•Glass molds , bearings
•Pistons
•Valve seats
|
| KF-Ni45 |
NiCrBSiFe |
0.45 |
13 |
3 |
10 |
2.5 |
Bal. |
HRC45 |
≤ 650ºC |
•Glass molds , bearings
•Pistons
•Valve seats
|
| KF-Ni55 |
NiCrBSiFe |
0.75 |
15 |
3 |
10 |
3 |
Bal. |
HRC 55 |
≤ 650ºC |
•Molds
•Bearings
•Pistons
|
| KF-Ni60B |
NiCrBSiFe |
0.80 |
17 |
4 |
15 |
3.5 |
Bal. |
HRC60 |
≤ 650ºC |
•Fan blades
•Boiler tubes
•Pistons
|
| KF-Ni60A |
NiCrBSiFe |
0.80 |
17 |
4 |
5 |
3.5 |
Bal. |
HRC 60 |
≤ 650ºC |
•Oxy-Acetylene, PTA, HVOF, APS, laser cladding, self-fluxing, spherical
•Pistons, conveying rollers, wire drawing pulling wheels, extrusion screw
•High hardness, wear and corrosion resistance
•Low frictional coefficient
|
| KF-Ni60AA |
NiCrBSiFe |
0.90 |
17 |
5 |
3 |
3.5 |
Bal. |
HRC60 |
≤ 650ºC |
•Oil coupling
•Conveyor roller
•Wire drawing pulling wheels,
•Extrusion screw
|
| KF-300A |
Ni60A+35WC-Ni |
Ni60A+35WC-Ni |
HRC65 |
≤ 600ºC |
•Oxy-Acetylene, PTA, HVOF, APS, laser cladding, self-fluxing, spherical
•Wire drawing pulling wheels, blades, pistons, impeller
•Better wear resistance than Ni60
•Self-fluxing
•Exellent particle abrasion and corrosion resistance
|
| KF-300B |
Ni60A+50WC-Co |
Ni60A+50WC-Co |
HRC65 |
≤ 600ºC |
•Brick machine
•Sediment agitation
•Extrusion screw
•Agricultural equipment
|
| KF-300C |
Ni60A+30WC-Co |
Ni60A+30WC-Co |
HRC65 |
≤ 600ºC |
•Oxy-Acetylene, PTA, HVOF, APS, laser cladding, self-fluxing, spherical
•Wire drawing pulling wheels, blades, pistons, impeller
•Better wear resistance than Ni60
•Exellent particle and hard facing abrasion and errosion resistance
|
| KF-300D |
Self-fluxing Nikel base Tugsten Carbide |
Proprietary |
HRC65 |
≤ 600ºC |
•Oxy-Acetylene, PTA, HVOF, APS, laser cladding, self-fluxing, spherical
•Wire drawing pulling wheels, blades, pistons, impeller
•Better wear resistance than Ni60
•Self-fluxing
•Exellent particle abrasion and corrosion resistance
|